WHITE Food Quality Neoprene Rubber 65° shore

SM 162 is a White FDA approved Neoprene rubber sheeting for use with food and drink stuffs. Neoprene material for use at higher temperatures for media containing oils, fats and greases.

On most sheetings we can offer the additional benefits of:-

Tacky - Back A bonding layer applied to one surface
Dry - Back Heavy Duty EP fabric layer on one or both sides
PU - Face A 2 or 3mm polyurethane coated surface layer

The above sheeting is manufactured from top quality virgin materials and ingredients meeting high standard of performance.

  • Material Profile: (see Data Sheet)
  • Thickness: 1.0mm to 10mm
  • Sheet Size: 1.4m wide in 10 and 20m rolls
  • Finish: Smooth finish,
  • Cutting: Standard press-tools
The component parts used and maximum levels in compound mixtures are in accordance with FDA [Food & Drug Administration – Department of Health and Human Services] part 177 – indirect food additives section 177.2600 – rubber articles for repeated use.

This Product is REACH, RoHS, PAH and CE Compliant

Other grades, colours and finishes are available - subject to minimum batch quantities

Your Search Results:

Material
Neoprene - Spec' Grade
Application
FDA APPROVED, Food / Drink, General Purpose
Shore Hardness +/- 5º
65
Thickness
1mm, 1.5mm, 2mm, 3mm, 4mm, 5mm, 6mm, 8mm, 10mm
Temp Range
-20°C, -10°C, +70°C, +80°C, +90°C, +100°C, +110°C, +120°C, +125°C, -25° C
Colour
White
Insertion Req
No
Cloth/Plate
Plate / Plate
Resistant To
Please Call

Technical Data

Stock Roll Sizes
[mm x mm x m]
Surface
Finish
Weight
[kg/M2]
Specifications
Compound
Values
[typical]
1.0mm x 1400mm x 20mSS 1.45ColourWhite
1.5mm x 1400mm x 10mSS  2.18CompoundCR
3mm x 1400mm x 10mSS 4.35Density [specific gravity]1.45
5mm x 1400mm x 10mSS7.25Hardness [Degrees Shore A]65° ± 5°
 6mm x 1400mm x 10m SS 8.70Tensile Strength Kg/cm2 [Polymer]50



Elongation at break250



Minimum Temperature-25°C



Maximum temperature+125°C



Compression Set (70°C for 22 hours) %35



 Polymer Content %100