Black High Temperature GENUINE Viton® (DuPont A) Rubber 75° shore

SM 149/75 Black High Temperature Genuine Viton® (DuPont A)Rubber 70° shore is a  Genuine Viton® (FKM) sheeting that has outstanding high resistance for high exposure applications with chemicals, acids, oils and petroleum products at high temperatures not achievable with other compounds.
SM149/75 has a 66% fluorine content

  • Material Profile: See below
  • Thickness: 0.5mm to 10mm
  • Sheet Size: 1.2m wide in 5m and 10m rolls
  • Finish: Smooth finish,
  • Cutting: Standard press-tools

Full specification sheet available on request

This Product is REACH, RoHS, PAH and CE Compliant


Other grades, colours and finishes are available - subject to minimum batch quantities

Your Search Results:

Material
Viton®
Application
Bio Diesel Resistant, Chemical Resistant, Diesel Resistant, Flame Resistant, Fuel Resistant, High Temperture, Oil / Fuel Resistant, Specification Grade, Weather / Ozone
Shore Hardness +/- 5º
75
Thickness
0.50mm, 1mm, 1.5mm, 2mm, 2.5mm, 3mm, 4mm, 5mm, 6mm, 8mm, 10mm
Temp Range
-20°C, -10°C, +70°C, +80°C, +90°C, +100°C, +110°C, +120°C, +125°C, +130° C, +140°C, +150°C, +160°C, +180°C, +200°C, +250°C and above, +170°C, +225° c
Colour
Black
Insertion Req
No
Cloth/Plate
Plate / Plate
Resistant To
Please Call

Technical Data

Stock Roll Sizes
[mm x mm x m]
Surface
Finish
Weight
[kg/M2]
Specifications
Compound
Values
[typical]
0.5mm x 1200mm x 10mSS 0.98ColourBlack
1mm x 1200mm x 0mSS  1.95CompoundDuPont Viton A
1.5mm x 1200mm x 10mSS 2.93Density [specific gravity]2,0
2mm x 1200mm x 10mSS3.90Hardness [Degrees Shore A]75° ± 5°
2.5mm x 1200mm x 10mSS4.88Tensile Strength Kg/cm2 [Polymer]50.00
3mm x 1200mm x 10mSS5.85Elongation at break200
4mm x 1200mm x 10mSS7.80Minimum Temperature-20°C
5mm x 1200mm x 10mSS9.75Maximum temperature+275°C
6mm x 1200mm x 10mSS11.70Compression Set (70°C for 22 hours) % 
8mm x 1200mm x 5mSS15.60 Polymer Content %100 
10mm x 1200mm x 5mSS19.50fluorine content %
 66